Catalytic dehydrogenation of methylcyclohexane (MCH) to toluene in a palladium/alumina hollow fibre membrane reactor
Date
2013Author
Mohd Irfan Hatim, Mohamed Dzahir, Dr.
Umi Fazara, Md. Ali, Dr.
Muhammad Syarhabil, Ahmad, Dr.
Fahmi, Muhammad Ridwan, Dr.
Metadata
Show full item recordAbstract
A compact multifunctional Pd/alumina hollow fibre membrane reactor (HFMR) has been developed and used for the catalytic dehydrogenation of methylcyclohexane to toluene. The developed HFMR consists of a thin and defect-free Pd membrane of 5 um coated directly onto the outer surface of an alumina hollow fibre substrate. The substrate, was prepared by a phase inversion/sintering method, possess a unique asymmetric structure which can be characterised by a very porous inner surface from which finger-like voids extend across approximately 80 % of the fibre cross-section with the remaining 20 % consisting of a denser sponge-like outer layer. A 50 wt% Ni/Al2O 3 catalyst is directly deposited into the asymmetric support, with a fraction of catalyst particles distributed uniformly in the finger-like macro-voids while the others on the lumen surface forming a "filter- cake"-like layer. A significant increase in gas permeation resistance occurs due to this "filter-cake"-like catalyst layer when the catalyst loading (weight per unit fibre length) is above 2.3 mg-cm-1. Methylcyclohexane conversion increases with the increasing temperatures, because of the endothermic nature of the reaction; while decreases with the higher sweep gas flow rates due to the more serious catalyst deactivation in the HFMR. For a HFMR with 1.0 mgx-1 of catalyst loading, methylcyclohexane conversion of approximately 26% can be achieved at 610 °C with the sweep gas flowrate of 20 ml min-1, while for a porous membrane reactor and a fixed-bed reactor the methylcyclohexane conversion of 50% and 25% can be achieved at identical operating temperature.