| dc.description | International Conference on Applications and Design in Mechanical Engineering 2012 (ICADME 2012) organized by School of Mechatronic Engineering, Universiti Malaysia Perlis (UniMAP), 27th - 28th Februari 2012 at Bayview Beach Resort, Penang, Malaysia. | en_US |
| dc.description.abstract | This paper present the effect of different duration aging
temperature on fatigue strength of Al6063. Al 6063 alloy
specimens have been solution heat treated at 520C for 2
hours. Subsequently, the artificial ageing heat treatment was
carried put at 200C ageing temperature at 4, 8 and 12 hours
respectively. Besides that, there are specimens that not been
to heat treatment process. The hardness test was carried out
where it shows that specimen at 8 hour ageing temperature
have the highest hardness test result compared with other
different ageing time. After that, the fatigue test was carried
out. From the fatigue test, graph stress versus number of
cycles was plotted. The result of S-N graph, it was found out
that 8 hour ageing temperature showed the highest fatigue
failure. Fractography studies via scanning electron
microscopy (SEM) revealed that there is a clearly striation
and crack growth appeared on the microstructure of the
specimen failure. | en_US |
| dc.language.iso | en | en_US |
| dc.publisher | Universiti Malaysia Perlis (UniMAP) | en_US |
| dc.relation.ispartofseries | Proceedings of the International Conference on Applications and Design in Mechanical Engineering 2012 (ICADME 2012) | en_US |
| dc.subject | Aluminum alloy 6063 | en_US |
| dc.subject | Fatigue strength | en_US |
| dc.subject | Ageing heat treatment | en_US |
| dc.subject | Scanning electron microscope (SEM) | en_US |
| dc.title | The effect of duration aging temperature on fatigue strength of aluminum alloy strength of aluminum alloy | en_US |
| dc.type | Working Paper | en_US |
| dc.publisher.department | Pusat Pengajian Kejuruteraan Mekatronik | en_US |
| dc.contributor.url | syayuthi@unimap.edu.my | en_US |