    Mechanical properties of ZTA composite using cold isostatic pressing and uniaxial pressing

    Thumbnail
    View/Open
    Mechanical properties of ZTA composite using cold isostatic pressing and uniaxial pressing.pdf (11.88Kb)
    Date
    2013
    Author
    Mohd Mustafa Al-Bakri, Abdullah
    Ahmad Fauzi, Mohd Noor, Prof. Dr
    Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.
    Norazian, Mohamed Noor
    Mohd Arif Anuar, Mohd Salleh
    Alida, Abdullah
    Metadata
    Show full item record
    Abstract
    Alumina-zirconia composite is an engineering material with a great potential to be develop for application as high temperature resistance structural material. In this research, zirconia toughness alumina (ZTA) was produced by physical interaction between Al2O3 powder and Y2O3-ZrO2 powder. Two composition of powder with different Al2O3: Y2O3-ZrO2 ratio was used, 70:30 and 80:20 by weight. Two different compaction methods, i.e. uniaxial pressing and cold isostatic pressing (CIP) with a maximum load of 150 MPa were used in this research to investigate the differences in properties of composites. Sintering process was done at four different temperatures with the heating rate is 5 °C/ min with a soaking time of five hours. Mechanical testing, i.e. compressive strength and hardness was performed to all samples. The microstructure analysis using a Scanning Electron Microscope SEM was also studied. From the result, the composite with the ratio of 70:30 showed better mechanical properties as compared to 80:20 composite. Addition of zirconia in the composite gave an increased in toughness due to transformation toughening mechanism of tetragonal to monoclinic phase. As a conclusion the composites produced high compaction green density will improved the sintering process, resulting in improved mechanical properties
    URI
    http://www.scientific.net/AMR.740.728
    http://dspace.unimap.edu.my:80/dspace/handle/123456789/32488
    Collections
    • Mohd Mustafa Al Bakri Abdullah, Prof. Dr. [277]
    • Alida Abdullah, Ts. Dr. [25]
    • Norazian, Mohamed Noor, Ts. Dr. [19]
    • School of Materials Engineering (Articles) [553]
    • Kamarudin Hussin, Brig. Jen. Datuk Prof. Dr. [252]
    • School of Environmental Engineering (Articles) [125]

    Atmire NV

    Perpustakaan Tuanku Syed Faizuddin Putra (PTSFP) | Send Feedback
     

     

    Browse

    All of UniMAP Library Digital RepositoryCommunities & CollectionsBy Issue DateAuthorsTitlesSubjectsThis CollectionBy Issue DateAuthorsTitlesSubjects

    My Account

    LoginRegister

    Statistics

    View Usage Statistics

    Atmire NV

    Perpustakaan Tuanku Syed Faizuddin Putra (PTSFP) | Send Feedback